Ceramic glaze is an impervious layer or coating of a vitreous substance which has been fused to a ceramic body through firing. Glaze can serve to color, decorate or waterproof an item. Glazing renders earthenware vessels suitable for holding liquids, sealing the inherent porosity of terracotta, the term we now use for basic unglazed earthenware. It also gives a tougher surface. Glaze is also used on stoneware and porcelain. In addition to their functionality, glazes can form a variety of surface finishes, including degrees of glossy or matte finish and color. Glazes may also enhance the underlying design or texture either unmodified or inscribed, carved or painted.
Most pottery produced in recent centuries has been glazed. Tiles are almost always glazed, and modern architectural terracotta is very often glazed architectural terra-cotta. Glazed brick is also common. Domestic sanitary ware is invariably glazed, as are many ceramics used in industry, for example ceramic insulators for overhead power lines.
The most important groups of traditional glazes, named after their main ceramic fluxing agent, are:
- Lead-glazed earthenware, is shiny and transparent after firing, which only needs about 800 °C (1,470 °F). Used for about 2,000 years around the Mediterranean, in Europe and China. Includes sancai and Victorian majolica.
- Tin-glazed pottery, which coats the ware with an opaque white glaze. Known in the Ancient Near East and then important in Islamic pottery, from which it passed to Europe. Includes faience, maiolica, majolica and Delftware.
- Salt-glazed ware, mostly European stoneware. It uses ordinary salt.
- Ash glaze, important in East Asia, simply made from wood or plant ash, which contains potash and lime.
- Feldspathic glazes of Asian porcelain.
Modern materials technology has invented new vitreous glazes that do not fall into these traditional categories.
Glazes need to include a ceramic flux which functions by promoting partial liquefaction in the clay bodies and the other glaze materials. Fluxes lower the high melting point of the glass formers silica, and sometimes boron trioxide. These glass former may be included in the glaze materials, or may be drawn from the clay beneath.
Raw materials of ceramic glazes generally include silica, which will be the main glass former. Various metal oxides, such as sodium, potassium and calcium, act as a flux to lower the melting temperature. Alumina, often derived from clay, stiffens the molten glaze to prevent it from running off the piece. Colorants, such as iron oxide, copper carbonate or cobalt carbonate, and sometimes opacifiers such as tin oxide or zirconium oxide, are used to modify the visual appearance of the fired glaze.
Glaze may be applied by dry-dusting a dry mixture over the surface of the clay body or by inserting salt or soda into the kiln at high temperatures to create an atmosphere rich in sodium vapor that interacts with the aluminium and silica oxides in the body to form and deposit glass, producing what is known as salt glaze pottery. Most commonly, glazes in aqueous suspension of various powdered minerals and metal oxides are applied by dipping pieces directly into the glaze. Other techniques include pouring the glaze over the piece, spraying it onto the piece with an airbrush or similar tool, or applying it directly with a brush or other tool.
To prevent the glazed article from sticking to the kiln during firing either a small part of the item is left unglazed, or supported on small refractory supports called kiln spurs which are removed and discarded after the firing. Small marks left by these spurs are sometimes visible on finished ware.
Decoration applied under the glaze on pottery is generally referred to as underglaze. Underglazes are applied to the surface of the pottery, which can be either raw, "greenware", or "biscuit"-fired (an initial firing of some articles before the glazing and re-firing). A wet glaze—usually transparent—is applied over the decoration. The pigment fuses with the glaze, and appears to be underneath a layer of clear glaze. An example of underglaze decoration is the well-known "blue and white" porcelain famously produced in England, the Netherlands, China and Japan. The striking blue color is achieved by using cobalt in the form of either cobalt oxide or cobalt carbonate, both of which are still commonly used.
Decoration applied on top of a layer of glaze is referred to as overglaze. Overglaze methods include applying one or more layers or coats of glaze on a piece of pottery or by applying a non-glaze substance such as enamel or metals (e.g., gold leaf) over the glaze.
Overglaze colors are low-temperature glazes that give ceramics a more decorative, glassy look. A piece is fired first, this initial firing being called the glost firing, then the overglaze decoration is applied, and it is fired again. Once the piece is fired and comes out of the kiln, its texture becomes smoother because of the glaze.
Historically, glazing of ceramics developed rather slowly, as appropriate materials needed to be discovered, and also firing technology able to reliably reach the necessary temperatures was needed.
Lead glazed earthenware was probably made in China during the Waring States Period (475 - 221 BCE), and its production increased during the Han Dynasty. High temperature proto-celadon glazed stoneware was made earlier than glazed earthenware, since the Shang Dynasty (1600 - 1046 BCE).
During the Kofun period of Japan, Sue ware was decorated with greenish natural ash glazes. From 552 to 794 AD, differently colored glazes were introduced. The three colored glazes of the Tang Dynasty were frequently used for a period, but were gradually phased out; the precise colors and compositions of the glazes have not been recovered. Natural ash glaze, however, was commonly used throughout the country.
In the 13th century, flower designs were painted with red, blue, green, yellow and black overglazes. Overglazes became very popular because of the particular look they gave ceramics.
From the eighth century, the use of glazed ceramics was prevalent in Islamic art and Islamic pottery, usually in the form of elaborate pottery. Tin-opacified glazing was one of the earliest new technologies developed by the Islamic potters. The first Islamic opaque glazes can be found as blue-painted ware in Basra, dating to around the 8th century. Another significant contribution was the development of stoneware, originating from 9th century Iraq. Other centers for innovative ceramic pottery in the Islamic world included Fustat (from 975 to 1075), Damascus (from 1100 to around 1600) and Tabriz (from 1470 to 1550).
As of 2012, over 650 ceramic manufacturing establishments were reported in the United States. Floor tile, wall tile, sanitary-ware, bathroom accessories, kitchenware, and tableware are all potential ceramic-containing products that are available for consumers. Heavy metals are dense metals used in glazes to produce a particular color or texture. Glaze components are more likely to be leached into the environment when non-recycled ceramic products are exposed warm or acidic water. Leaching of heavy metals occur when ceramic products are glazed incorrectly or damaged. Lead and chromium are two heavy metals commonly used in ceramic glazes that are heavily monitored by government agencies due to their toxicity and ability to bioaccumulate.
Metal oxide chemistry
Metals used in ceramic glazes are typically in the form of metal oxides.
Ceramic manufacturers primarily use lead(II) oxide (PbO) as a flux for its low melting range, wide firing range, low surface tension, high index of refraction, and resistance to devitrification. Nitrogen dioxide (NO
2) plays a role in the mobilization of lead in the environment. In polluted environments, nitrogen dioxide reacts with water (H
2O) to produce nitrous acid (HNO
2) and nitric acid (HNO
2O + 2NO
2 → HNO
2 + HNO
Lead(II) nitrate (Pb(NO
2) forms when lead(II) oxide (PbO) of leaded glazes is exposed to nitrogen dioxide (NO
2) found in polluted air.
PbO + 2HNO
3 → Pb(NO
2 + H
2 → Pb2+
When consumed, lead interferes with normal biochemistry by forming stable chemical bonds with amino acids of proteins. When lead is converted to its stable oxidation state (Pb2+), it reacts with the sulphydryl groups (-SH) of cysteine. Proteins bound to lead are unable to be used up by biological processes remain in the tissue of plants and animals.
Chromium(III) oxide (Cr
3) is used as a colorant in ceramic glazes. Chromium(III) oxide can undergo a reaction with calcium oxide (CaO) and atmospheric oxygen in temperatures reached by a kiln to produce calcium chromate (CaCrO
4). The oxidation reaction changes chromium from its +3 oxidation state to its +6 oxidation state. Chromium(VI) is very soluble and the most mobile out of all the other stable forms of chromium.
Chromium may enter water systems via industrial discharge. Chromium(VI) can enter the environment directly or oxidants present in soils can react with chromium(III) to produce chromium(VI). Plants have reduced amounts of chlorophyll when grown in the presence of chromium(VI).
Chromium oxidation during manufacturing processes can be reduced with the introduction of compounds that bind to calcium. Ceramic industries are reluctant to use lead alternatives since leaded glazes provide products with a brilliant shine and smooth surface. The United States Environmental Protection Agency has experimented with a dual glaze, barium alternative to lead, but they were unsuccessful in achieving the same optical effect as leaded glazes.
Meissen porcelain, with blue underglaze decoration on porcelain
Mug with blue underglaze decoration on porcelain.
Test slabs of different glazes
20th century glazing technique
- Division, Company Statistics. "Statistics of U.S. Businesses Main Page". www.census.gov. Retrieved 2015-11-27.
- "Cleaning Biscuit Fired Ceramic Ware" Hulse D.K, Barnett W.C. UK Pat.Appl.GB2287643A
- Denio, Allen A. (1980-04-01). "Chemistry for potters". Journal of Chemical Education. 57 (4). doi:10.1021/ed057p272.
- "Roller Kilns For The Fast Biscuit And Glost Firing Of Porcelain" Rodriguez Mamolar M.J., De La Fuente Revuelta J. Ceram. Inf.(Spain) 20, No.202. 1994. Pg. 25–27
- 'Ceramics Glaze Technology.' J.R.Taylor & A.C.Bull. The Institute Of Ceramics & Pergamon Press. Oxford. 1986
- Daiheng, Gao (2002). Chinese Architecture -- The Lia, Song, Xi Xia and Jin Dynasties (English ed.). Yale University Press. pp. 166, 183. ISBN 0-300-09559-7.
- Zhiyan, Li (2002). Chinese Ceramics -- From the Paleolithic Period through the Qing Dynasty (English ed.). New York & London, Beijing: Yale University Press, Foreign Languages Press. pp. 144, 145, 152. ISBN 978-0-300-11278-8.
- Environment, Department of the. "Nitrogen dioxide (NO2)". www.environment.gov.au. Retrieved 2015-11-09.
- Mason (1995), p. 5
- Missoun, F., M. Slimani, and A. Aoues. "Toxic Effect of Lead on Kidney Function in Rat Wistar." African Journal of Biochemistry Research 4.2 (2010): 21–27. Print.
- Environmental Protection Agency. (February 2003) Economic Impact Analysis of the Clay Ceramics Manufacturing NESHAP: Final Rule (EPA Publication No. EPA-452/R-03-007). Research Triangle Park, NC: Environmental Protection Agency.
- Omolaoye, J.A,, A. Uzairu, and C.E. Gimba. "Heavy Metal Assessment of Some Ceramic Products Imported into Nigeria from China." Archives of Applied Science Research 2.5 (2010): 120-25. Web. 15 Oct. 2015
- Baltrusaitis, Jonas; Chen, Haihan; Rubasinghege, Gayan; Grassian, Vicki H. (2012-12-04). "Heterogeneous Atmospheric Chemistry of Lead Oxide Particles with Nitrogen Dioxide Increases Lead Solubility: Environmental and Health Implications". Environmental Science & Technology. 46 (23): 12806–12813. doi:10.1021/es3019572. ISSN 0013-936X. PMC 3518381. PMID 23057678.
- Lehman, Richard. Lead Glazes for Ceramic Foodware. 1st ed. Research Triangle Park: International Lead Management Center, 2002. International Lead Management Center
- Duruibe, J.O., M.O.C. Ogwuegbu, and J.N. Egwurugwu. "Heavy Metal Pollution and Human Biotoxic Effects." International Journal of Physical Sciences 2.5 (2007): 112-18.
- Verbinnen, Bram; Billen, Pieter; Van Coninckxloo, Michiel; Vandecasteele, Carlo (2013-06-04). "Heating Temperature Dependence of Cr(III) Oxidation in the Presence of Alkali and Alkaline Earth Salts and Subsequent Cr(VI) Leaching Behavior". Environmental Science & Technology. 47 (11): 5858–5863. doi:10.1021/es4001455. ISSN 0013-936X.
- Oliveira, Helena (2012-05-20). "Chromium as an Environmental Pollutant: Insights on Induced Plant Toxicity". Journal of Botany. 2012: 1–8. doi:10.1155/2012/375843.
- Hamer, Frank and Janet. The Potter's Dictionary of Materials and Techniques. A & C Black Publishers, Limited, London, England, Third Edition 1991. ISBN 0-8122-3112-0.